Effect of ball size on the microstructure and morphology of mg powders processed by high-energy ball milling
Cargando...
Compartir
Fecha
Título de la revista
ISSN de la revista
Título del volumen
Editor
MDPI
Resumen
Descripción
Commercial powders of pure magnesium were processed by high-energy ball milling. The microstructural and morphological evolution of the powders was studied using scanning electron microscopy (SEM), energy dispersive spectrometry (EDX) and X-ray diffraction (XRD). From the results obtained, it was determined that the ball size is the most influential milling parameter. This was because balls of 1 mm diameter were used after a previous stage of milling with larger balls (i.e., 10 and 3 mm). The powder particles presented an unusual morphology with respect to those observed in the Mg-milling literature and recrystallization phenomena. Moreover, the result strongly varied depending on the ball-to-powder weight ratio (BPR) used during the milling process. © 2021 by the authors. Licensee MDPI, Basel, Switzerland.